Dongshang Stainless manufactures ASTM B622/ASME SB622 C276 N10276 Seamless Tube in a cold-drawn seamless process, Pipe and tube shall be supplied in the solution annealed and descaled condition. When atmosphere control is used, descaling is not necessary. This specification is limited to tubes up to and including 3.5 in. (88.9 mm) outside diameter. Beveled ends or plain ends and deburred will be furnished.
Hastelloy C276, UNS N10276, WERKSTOFF NR. 2.4819, EN NiMo16Cr15W, JIS NW 0276, GOST ХН65МВУ
ASTM B622 Hastelloy UNS N10276 Seamless Tube, ASTM B622 Hastelloy Pipes, ASTM B622 Hastelloy C276 Seamless Pipe, ASME SB622 Tubes Supplier in China. ASTM B622 Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube Size range from 0.5 mm to 12.7 mm, Hastelloy C276 Pipes, ASTM B622 Hastelloy Seamless Pipe, ASTM B622 Pipe, ASME SB622 Hastelloy Tubing Manufacturer in China.
ASTM B622 UNS N10276 Hastelloy C276 Seamless Pipe Description
| Standard | ASTM B622, ASME SB622 |
|---|---|
| Tube Type | Seamless Tube |
| Alloy | UNS N10276, C276 |
| Finishing | Annealing Pickling, Bright Annealing |
| Outside Diameter | NPS from 1/4 To 3 |
| Thickness | Schedule No. 10, Schedule No. 40, Schedule No. 80 |
ASME B622 /ASME SB622 UNS N10276 Hastelloy C276
ASTM B622 – Standard Specification For Seamless Nickel And Nickel-Cobalt Alloy Pipe And Tube
ASME B622 /ASME SB622 UNS N10276, A nickel-molybdenum-chromium-iron-tungsten alloy, Low C Ni-Cr-Mo alloy C-276, C276 exhibits excellent corrosion resistance in a wide range of severe environments.
Hastelloy C276 is a nickel-molybdenum-chromium superalloy with an addition of tungsten designed to have excellent corrosion resistance in a wide range of severe environments. The high nickel and molybdenum contents make the nickel steel alloy especially resistant to pitting and crevice corrosion in reducing environments while chromium conveys resistance to oxidizing media. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures. This nickel alloy is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in an as welded condition.
Although there are several variations of the Hastelloy nickel alloy, Hastelloy C-276 is by far the most widely used.
Alloy C-276 is widely used in the most severe environments such as chemical processing, pollution control, pulp and paper production, industrial and municipal waste treatment, and recovery of sour natural gas.
ASTM B622 ASME SB 622 UNS N10276 C276 Chemical Composition
| Alloy | Ni | Cr. | Mo | Fe | W | Co | C | Mn | Si | V | P | S |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| N10276 (C276) | Remainder | 14.5-16.5 | 15.0-17.0 | 4.0-7.0 | 3.0-4.5 | 2.5 | 0.010 | 1.0 | 0.08 | 0.35 | 0.04 | 0.03 |
Composition Limits, %, range limit or max.
ASTM B622 ASME SB 622 UNS N10276 C276 Mechanical Properties
| Alloy | Yield Strength | Tensile Strength | Elongation | Hardness |
|---|---|---|---|---|
| Min, Ksi (MPa) | Min, Ksi (MPa) | Min, % | ||
| UNS N10276 | 100 (690) | 41 (283) | 40 | 87 HRB |
Characteristics Of Hastelloy C276?
- Excellent corrosion resistance in reducing environments
- Exceptional resistance to strong solutions of oxidizing salts, such as ferric and cupric chlorides
- High nickel and molybdenum contents provide good corrosion resistance in reducing environments
- Low carbon content which minimizes grain-boundary carbide precipitation during welding to maintain resistance to corrosion in heat-affected zones of welded joints
- Resistance to localized corrosion such as pitting and stress-corrosion cracking
- One of few materials to withstand the corrosive effects of wet chlorine gas, hypochlorite and chlorine dioxide
Material Testing
• Mechanical Testing Such as Tensile of Area
• Hardness Test
• Chemical Analysis – Spectro Analysis
• Positive Material Identification – PMI Testing
• Flattening Test
• Micro and MacroTest
• Pitting Resistance Test
• Flaring Test
• Intergranular Corrosion (IGC) Test
C276 UNS 10276 Alloy Specifications
ASTM B622 – Standard Specification For Seamless Nickel And Nickel-Cobalt Alloy Pipe And Tube
ASTM B619/B619M – Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe
ASTM B626-Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube
ASTM B575 – Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, Low-Carbon Nickel-Chromium-Molybdenum-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Tungsten, and Low-Carbon Nickel-Molybdenum-Chromium
ASTM B574 – Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten
ASTM B366/B366M – Standard Specification for Factory-Made Wrought Nickel and Nickel Alloy Fittings